SX1,SX2,SX8,SP2 Si3N4
Type
 |
Mainly composed
of silicon nitride (Si3N4), these inserts with excellent
toughness and wear resistance are stable during rough
turning and milling of cast iron with coolant. Their
performance during rough turning is outstanding. |
|
Applications |
| |
rough turning
and milling of gray cast iron |
|
|
|
|
 |
|
HC1,Hw2 Al2O3 Type
|
|
Mainly composed of highly pure alumina (Al2O3), these
inserts have a very dense fine grain structure and have
superior wear resistance and fracture toughness. |
|
Applications |
| |
General
turning and boring of gray cast iron Tube scarfing |
|
|
|
|
 |
|
HC2,HC4<HC5 Al2O3-TiC Type
|
|
Its excellent
hight temperature hardness and reduced plastic deformation
allows a wide range of applications including finish
machining of hardened materials. HC5 has superior
performance in roll turning. |
|
Applications |
| |
General
turning and boring of gray cast iron Turning of heat
resistant alloys Turning of hard materials (under HRC65) |
|
|
|
|
 |
|
T3N,T15,C30,C50,N20,N40 Cermet
|
|
NTK cermet
series is lined up by TiC-Ti based T3N, T15, C30, has
great wear resistance. C50 has excellent thermal shock
resistance.N20, N40 have great toughness and wear
resistance. |
|
Applications |
| |
Semi-finish
and grooving of steel Turning of bearing parts and general
milling |
|
|
|
|
 |
|
Z15,Z50,Q15Q50 PVD Coated Cermet
|
|
These grades
are coated by PVD to improve ear resistance. |
|
Applications |
| |
Semi-finish
and finishing turning of steel and ductile cast iron. |
|
|
|
|
 |
|
B20,B22,B24
|
|
These inserts,
composed of CBN (Cubic Boron Nitride) and special ceramic
binder, have high hardness at room temperature and high
temperatures and less affinity to work piece materials,
allowing efficient high speed machining of hardened steels
and gray cast iron. |
|
Applications |
| |
High speed
finish turning of hard materials (over HRC60) and gray
cast iron with coolant. High speed milling of gray cast
iron |
|
|
|
|